   Ofluorine PVDF
T-1 PVDF for coatings
T-2 PVDF for powder coatings
D-1 PVDF Lithium Ion Battery Binders
Ofluorine 904 PVDF for UF membranes
 
J-2 PVDF Extrusion Grade
 
Z-1 PVDF Injection Grade
 
M-1 PVDF Moulding Grade
 
PVDF copolymer
 
PVDF film for solar back sheet
 
   
J-2 PVDF Extrusion Grade
pvdf for extrusion moulding
Medium melt viscosity,  more suitable for extrusion molding.
J-2 PVDF as raw materials, the finished products has excellent mechanical strength and flexibility. It can not be eroded by acid, alkali, strong oxidant, halogens. Good durability to aliphatic hydrocarbons, aromatic hydrocarbons, alcohol, aldehyde etc. In the work of hydrochloric acid, nitric acid, sulfuric acid, dilute alkali liquor, dense alkali liquor(40%) and 100deg.C, which keep stable.
Others, J-2 PVDF finished products has the properties of γ-Ray resistant, UV resistant, and stability in wide temperature range.
Application: Be used in manufacturing PVDF tubes, PVDF pipes, PVDF rod etc.mail to us

J-2 PVDF pellets technical data sheet

Properties

 Typical Values

Standard

Appearance 

            White translucent pellets 

Odor

None

Standard specific gravity

1.77-1.79

ASTM D792,at 23/23℃

Melting point

165-171℃

ASTM D3418,10℃/min

Melt flow index

10-25g/10min

ASTM D1238,230℃/12.5kg

Water absorption

≤0.05%

ASTM D570

Tensile yield strength

≥40MPa

ASTM D638,50mm/min at 23℃

Yield elongation

5-10%

ASTM D638,50mm/min at 23℃

Tensile strength at break

≥30MPa

ASTM D638,50mm/min at 23℃

Elongation at break

≥50%

ASTM D638,50mm/min at 23℃

Hardness,Shore D

70-80

ASTM D2240

Flammability test V-0 UL 94

Safety instructionpvdf tubing
J-2 PVDF is stable under 310deg.C. When it is stored at 310-320deg.C for a long time, trace toxic hydrogen fluoride(HF) and fluorocarbon organic chemicals(FC) begin to release, when the temperatures more than 370deg.C, HF and FC release speed up. So, a temperature below 310deg.C is suggested for processing and using J-2 PVDF.
Furthermore, although J-2 PVDF have good flame retardancy, in case of fire, HF and FC will also be released.

Packing
25kg/carton or 25kg/kraft bag

 